General Maintenance Coating & High Performance Maintenance Coatings
Harlepoxy Top Coat Industrial Grade 1
Grade |
Performance Grade |
Drying System |
Air Drying Top Coat |
Description |
It is a two pack finish paint based on Epoxy resin and polyamide curing agent. It gives a good protection in chemical and corrosive atmosphere. |
Volume Solids |
48 /-2 % |
DFT |
20-25 µm per coat |
Mixing Ratio |
BASE : HARDNER 4:1 OR 3:1 |
Pot Life |
4 Hrs Minimum |
Spreading Rate |
22-30 m²/L |
Hard Dry |
10-12 hrs @ 30°C and 65% relative humidity |
Surface Dry |
0.5-1 hr. @ 30°C and 65% relative humidity |
Tack Free |
Overnight |
Subsequent Coat |
As per substrate condition recommended coating system |
Recoating Time - MIN |
16 Hrs |
Recoating Time - MAX |
7 Days |
Finish |
Smooth Uniform Semi Glossy to matt |
Shelf Life |
Base: 1 year Hardner: 6 months |
Surface Preparation |
Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
Applicable Industry |
Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical |
Application Method |
Conventional Air Spray/ Brushing / Airless Spray |
Gel Time |
4 Hrs Minimum |
Recommended Thinner |
Harlepoxy Thinner |
Suggested Use |
For high quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants and Automobile Industry |
Harlepoxy Top Coat Industrial Grade 2
Grade |
Industrial Grade 2 |
Drying System |
Air Drying Top Coat |
Description |
It is a two pack finish paint based on Epoxy resin and poly amide or amine curing agent. It gives a excellent protection in chemical and corrosive atmosphere. |
Volume Solids |
42 /-2 % |
DFT |
20-25 µm per coat |
Mixing Ratio |
BASE : HARDNER 4:1 OR 3:1 |
Pot Life |
4 Hrs Minimum |
Spreading Rate |
17-21 m²/L |
Surface Dry |
1-1.5 hr. @ 30°C and 65% relative humidity |
Hard Dry |
12-14 hrs @ 30°C and 65% relative humidity |
Tack Free |
Overnight |
Subsequent Coat |
As per substrate condition recommended coating system |
Recoating Time - MIN |
16 Hrs |
Recoating Time - MAX |
7 Days |
Finish |
Smooth Uniform Semi Glossy to matt |
Shelf Life |
Base: 1 year Hardner: 6 months |
Surface Preparation |
Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
Applicable Industry |
Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical |
Application Method |
Conventional Air Spray/ Brushing / Airless Spray |
Gel Time |
4 Hrs Minimum |
Recommended Thinner |
Harlepoxy Thinner |
Suggested Use |
For Good quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants and Automobile Industry |
Harlepoxy Top Coat Maintenance Grade
Grade |
Industrial Grade 2 |
Drying System |
Air Drying Top Coat |
Description |
It is a two pack finish paint based on fortified Epoxy resin and polyamide curing agent. It gives a fair protection in chemical and corrosive atmosphere. With excellent drying and coverage property |
Volume Solids |
50 /-2 % |
DFT |
20-25 µm per coat |
Mixing Ratio |
BASE : HARDNER 4 : 1 OR 3:1 |
Pot Life |
6 Hrs Minimum |
Spreading Rate |
20-25 m²/L |
Surface Dry |
15-20mints. @ 30°C and 65% relative humidity |
Hard Dry |
12-14 hrs @ 30°C and 65% relative humidity |
Tack Free |
Overnight |
Subsequent Coat |
As per substrate condition recommended coating system |
Recoating Time - MIN |
16 Hrs |
Recoating Time - MAX |
7 Days |
Finish |
Smooth Uniform Full Glossy / Semi Glossy to matt |
Shelf Life |
Base: 1 year Hardner: 6 months |
Surface Preparation |
Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
Applicable Industry |
Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical |
Application Method |
Conventional Air Spray/ Brushing / Airless Spray |
Gel Time |
6 Hrs Minimum |
Recommended Thinner |
Harlepoxy Thinner |
Suggested Use |
For quality coating for Fabrication Industries, Machine Tool Industry, chemical industry, at economic cost etc |