| Grade | Performance Grade |
| Drying System | Air Drying Top Coat |
| Description | It is Two Pack Polyurethane coating based on special acrylic polyol and Aliphatic or aromatic Hardner |
| Volume Solids | 52 /-2 % |
| DFT | 20-25 µm per coat |
| Mixing Ratio | BASE : HARDNER 3:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 20-26 m²/L |
| Surface Dry | 1-1.5 Hrs. @ 30°C and 65% relative humidity |
| Hard Dry | 14-16 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 14 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform – Glossy or Semi glossy or Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter. |
| Applicable Industry | Wood |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For excellent quality Wood finishes, Fabrication Industries, Machine Tool Industry, Plastic Industry, Gift Articles and solvent and chemical industries ,Automobile Industry . * [ FOR BEST PERFORMANCE , DURABILITY and CHEMICAL RESISTNACE USE PERMIUM GRADE ] |
| Grade | Industrial Grade 1 |
| Drying System | Air Drying Top Coat |
| Description | It is Two Pack Polyurethane coating based on acrylic polyol and Aliphatic OR Aromatic orHardner |
| Volume Solids | 40 /-2 % |
| DFT | 20-25 µm per coat |
| Mixing Ratio | BASE : HARDNER 4:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 16-20 m²/L |
| Surface Dry | 20-30 min. @ 30°C and 65% relative humidity |
| Hard Dry | 12-14 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 14 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform – Glossy or Semi glossy or Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
| Applicable Industry | Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For good quality Wood finishes, Fabrication Industries, Machine Tool Industry, Plastic Industry, Gift Articles and solvent and chemical industries ,Automobile Industry .* [ FOR BEST PERFORMANCE , DURABILITY and CHEMICAL RESISTNACE USE PERMIUM GRADE ] |
| Grade | Industrial Grade 1 |
| Drying System | Air Drying Top Coat |
| Description | It is Two Pack Polyurethane coating based on Specialised acrylic polyol, additives and Aliphatic OR Aromatic Hardner |
| Volume Solids | 48 /-2 % |
| DFT | 20-25 µm per coat |
| Mixing Ratio | BASE : HARDNER 4:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 19-24 m²/L |
| Surface Dry | 10-15 min. @ 30°C and 65% relative humidity |
| Hard Dry | 6-8 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 14 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform – Glossy or Semi glossy or Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
| Applicable Industry | Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For good quality fast setting Wood finishes, Fabrication Industries, Machine Tool Industry, Plastic Industry, Gift Articles and solvent and chemical industries ,Automobile Industry.* [ FOR BEST PERFORMANCE , DURABILITY and CHEMICAL RESISTNACE USE PERMIUM GRADE ] |
| Grade | Industrial Grade 1 |
| Drying System | Air Drying Top Coat |
| Description | It is Two Pack Polyurethane coating based on polyester polyol and Aliphatic or Aromatic Hardner |
| Volume Solids | 50 /-2 % |
| DFT | 20-25 µm per coat |
| Mixing Ratio | BASE : HARDNER 9:1 Or 4:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 20-25 m²/L |
| Surface Dry | 1-2 Hrs. @ 30°C |
| Hard Dry | 14-16 hrs @ 30°C |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 14 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform – Glossy or Semi glossy or Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | "Recommended primed surface should be free from oil, grease, salt |
| Applicable Industry | Packaging/OEM Engineering/ General Maintainance/Electronic and Electrical |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Sugested Use | For high quality, Fabrication Industries, Machine Tool Industry, chemical plants, power plants, packagings and Automobile Industry. * [ FOR BEST PERFORMANCE , DURABILITY |
| Grade | Performance Grade |
| Drying System | Air Drying Top Coat |
| Description | It is Two Pack Polyurethane coating based on special acrylic polyol and Aliphatic or aromatic Hardner |
| Volume Solids | 52 /-2 % |
| DFT | 20-25 µm per coat |
| Mixing Ratio | BASE : HARDNER 3:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 20-26 m²/L |
| Surface Dry | 1-1.5 Hrs. @ 30°C and 65% relative humidity |
| Hard Dry | 14-16 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 14 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform – Glossy or Semi glossy or Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
| Applicable Industry | Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For excellent quality Wood finishes, Fabrication Industries, Machine Tool Industry, Plastic Industry, Gift Articles and solvent and chemical industries ,Automobile Industry . * [ FOR BEST PERFORMANCE , DURABILITY and CHEMICAL RESISTNACE USE PERMIUM GRADE ] |
| Grade | Industrial Grade 2 |
| Drying System | Air Drying Under Coat |
| Description | It is Two Pack Polyurethane coating based on polyester polyol and Aliphatic or Aromatic Hardner |
| Volume Solids | 40 /-2 % |
| DFT | 20-25 µm per coat |
| Mixing Ratio | BASE : HARDNER 4:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 16-20 m²/L |
| Surface Dry | 1-2 Hrs. @ 30°C and 65% relative humidity |
| Hard Dry | 14-16 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 14 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform – Glossy or Semi glossy or Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | Recommended primed surface should be free from oil, grease, salt and any other foreign matter. |
| Applicable Industry | Packaging/OEM Engineering/ General Maintainance/Electronic and Electrical |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For high quality, Fabrication Industries, Machine Tool Industry, chemical plants, power plants, packagings and Automobile Industry. * [ FOR BEST PERFORMANCE , DURABILITY and CHEMICAL RESISTNACE USE PERMIUM GRADE ] |
| Grade | Performance Grade |
| Drying System | Air Drying Under Coat |
| Description | It is Two Pack Polyurethane undercoat based on Acerylic polyol and Aromatic Hardner having very fast setting |
| Volume Solids | 52 /-2% |
| DFT | 30-35 µm per coat |
| Mixing Ratio | BASE : HARDNER 10:2 |
| Pot Life | 5 Hrs Minimum |
| Spreading Rate | 12-14 m²/L |
| Surface Dry | 25-30 mints. @ 30°C and 65% relative humidity ( Sanding Time 2-3 hrs ) |
| Hard Dry | 6-8 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 8 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter. |
| Applicable Industry | Packaging/OEM Engineering/ General Maintainance/Electronic and Electrical |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For Good quality, Fabrication Industries, Machine Tool Industry, chemical plants, packagings industry, etc. |
| Grade | Performance Grade |
| Drying System | Quick Drying Under CoatIt is Two Pack Polyurethane sealer based on Specialised acrylic polyol, fillers additives and Aromatic Hardner 50 /-2 % Smooth and Uniform - Matt30-35 µm per coat14-17 m²/L 10-15 min. @ 30°C |
| Description | It is Two Pack Polyurethane sealer based on Specialised acrylic polyol, fillers additives and Aromatic Hardner |
| Volume Solids | 50 /-2 % |
| DFT | 30-35 µm per coat |
| Mixing Ratio | BASE : HARDNER 10:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 14-17 m²/L |
| Surface Dry | 10-15 min. @ 30°C and 65% relative humidity ( Sanding Time 2 Hrs. ) |
| Hard Dry | 6-8 hrs @ 30°C and 65% relative humidity depending |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 8 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform - Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | Recommended wooden surface should be free from oil, grease, salt, dust and any other foreign matter. |
| Applicable Industry | Wood |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Gel Time | 4 Hrs Minimum |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For excellent quality fast setting Wood sealer. |
| Grade | Performance Grade |
| Drying System | Air Drying Under Coat |
| Description | It is Two Pack Polyurethane undercoat based on polyester polyol and Aromatic Hardner having very fast setting and sanding properties and compatibility with various coating system. |
| DFT | 30-35 µm per coat |
| Volume Solids | 42 /-2 % |
| Mixing Ratio | BASE : HARDNER 10:1 |
| Pot Life | 4 Hrs Minimum |
| Spreading Rate | 12-14 m²/L |
| Surface Dry | 25-30 mints. @ 30°C and 65% relative humidity ( Sanding Time 2-3 hrs ) |
| Hard Dry | 6-8 hrs @ 30°C and 65% relative humidity |
| Tack Free | Overnight |
| Subsequent Coat | As per substrate condition recommended coating system |
| Recoating Time - MIN | 8 Hrs |
| Recoating Time - MAX | 7 Days |
| Finish | Smooth and Uniform Matt |
| Shelf Life | Base: 1 year Hardner: 6 months |
| Surface Preparation | New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter. |
| Applicable Industry | Base: 1 year Hardner: 6 months |
| Application Method | Conventional Air Spray/ Brushing / Airless Spray |
| Recommended Thinner | Harlecoat Thinner |
| Suggested Use | For Good quality, Fabrication Industries, Machine Tool Industry, chemical plants, packagings industry, etc. |
20 & 21, Universal Industrial Estate, Sajgoan
Taluka: Khalapur District: RaigadState:Maharashtra - 410 203
Factory: (02192) 263244