| Description | It is a two pack Epoxy based clear coating. |
| Volume Solids | 42% ± 2 |
| DFT | 25 microns |
| Mixing Ratio | BASE HARD. 4 : 1 |
| Pot Life | 5 - 6 hrs. at 30OC and 65% relative humidity |
| Spreading Rate | 17 sq.m/ltr. |
| Surface Dry | 1 - 2 hrs. at 30OC and 65% relative humidity |
| Hard Dry | 8 hrs. at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 8 hrs. at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | 4 days |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | "Concrete Surface: Should be free from laitance and other contaminants. So also surface is to be cleaned by sweep blast or treat with power tools to obtain rough and firm surface. If concrete is new check for alklinity of concrete surface and if found to alkaline treat with dilute hydrochloric acid and then to be clean with fresh water till the pH of washing is in between 6-7. Remove oil, grease or any foreign matters by suitable means. " |
| Applicable Industry | Maintanance |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | Used as a primer over concrete. Also can be used to over coat aged epoxy surface. after removal of loose paint and dust from surface. |
| Description | It is a two pack Epoxy base high build coating for metal and concrete surfaces. It is a surface tolerant self priming coating having good chemical resistance and moisture tolerance. |
| Volume Solids | 80% ± 2 |
| DFT | 100-125 Microns |
| Mixing Ratio | BASE HARD. 4 : 1 |
| Pot Life | 4 hrs. at 30OC and 65% relative humidity |
| Spreading Rate | 6.5 – 8 Sq.m/ltr |
| Surface Dry | 3 hrs. at 30OC and 65% relative humidity |
| Hard Dry | 10 hrs. at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 16 Hrs at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | 3 months |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | "New Steel: Recommended for abrasive blasting to Sa2½. If steel is coated by shop primer, clean all damages to shop primer and also clean the surface free from oil grease and any other foreign particles. Maintenance: Remove oil, grease etc with a detergent wash. Remove salt and other contaminants by high pressure fresh water hosing. Remove all rust and loose materials by abrasive blasting or mechanical cleaning. Dust off residues. For best results remove all loose rust by wire brushing and chipping. " |
| Applicable Industry | Maintanance |
| Application Method | Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | To use in varied conditions for protection of all types of metal surfaces. This can be used on manually cleaned surface where blasting is not possible. |
| Description | It is a two pack shop coat primer based on Epoxy resin and Red Oxide pigment. It gives protection to the cut and weld exposed surface from corrosion with no problem in cutting and welding of steel. Generally it protects steel from corrosion for 6 - 7 months. |
| Volume Solids | 35% ± 2 |
| DFT | 25 microns |
| Mixing Ratio | BASE HARD. 3 : 1 |
| Pot Life | 5-6 hrs. at 30OC and 65% relative humidity |
| Spreading Rate | 13 -15 sq.m. / ltr. |
| Surface Dry | 10 - 15 min at 30OC and 65% relative humidity |
| Hard Dry | 4-6 hrs. at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 24 hrs. at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | None |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | "Recommended surface should be free from oil, grease, salt and any other foreign matter Blast clean to Sa2½ minimum with Surface profile not more than 75 Microns. " |
| Applicable Industry | Maintanance / OEM |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | Generally used as prefabrication primer for steel surfaces. It can be used as a primer for steel structures in severe corrosive conditions. |
| Description | It is a two pack primer based on Epoxy resins. It gives excellent corrosion resistance properties |
| Volume Solids | 50% ± 2 |
| DFT | 60 - 70 microns |
| Mixing Ratio | BASE HARD. 4 : 1 |
| Pot Life | 6-7 hrs. at 30OC and 65% relative humidity |
| Spreading Rate | 7 - 9 sq.m/ltr. |
| Surface Dry | 2-3 hrs. at 30OC and 65% relative humidity |
| Hard Dry | 8 hrs. at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 18 hrs. at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | 7 days |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | Recommended surface should be free from oil, grease, salt and any other foreign matter. Blast cleaned / Power tool cleaning preferred. For new surface blast cleaning Sa2½ is recommended |
| Applicable Industry | Maintanance /OEM |
| Application Method | Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | Can be used directly on a steel surface and compatible with shop primer. |
| Description | It is a two pack pre-welding or shop coat primer based on Epoxy resin and Zinc Dust. It gives protection to the cut and weld exposed surface from corrosion with no problem in cutting and welding of steel. Generally it protects steel from corrosion for 6-7 months. |
| Volume Solids | 35 % ± 2 |
| DFT | 25 microns13 - 15 sq.m./ltr. |
| Mixing Ratio | BASE HARD. 3 : 1 |
| Pot Life | 8 Hrs at 30OC and 65% Relative Humidity |
| Spreading Rate | 13 - 15 sq.m./ltr. |
| Surface Dry | 7 -10 min at 30OC and 65% relative humidity |
| Hard Dry | 6 - 8 hrs. at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 18 hrs. at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | None |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | "Recommended surface should be free from oil, grease, salt and any other foreign matter Blast clean to Sa2½ minimum with Surface profile not more than 75 Microns. " |
| Applicable Industry | Maintanance /OEM |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | Generally used as prefabrication primer for steel surfaces. It can be used as a primer for steel structures in severe corrosive conditions. |
| Description | It is a two pack primer based on Epoxy resin and Zinc Dust. Zinc content is 80% on dry film thickness. |
| Volume Solids | 45% ± 2 |
| DFT | 25 microns |
| Mixing Ratio | BASE HARD. 3 : 1 |
| Pot Life | 8 hrs. at 30OC and 65% relative humidity |
| Spreading Rate | 17-19 Sq.m/ltr |
| Surface Dry | 7-10 min. at 30OC and 65% relative humidity |
| Hard Dry | 6-8 hrs. at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 24 hrs. at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | None |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | "Recommended surface should be free from oil, grease, salt and any other foreign matter Blast clean to Sa2½ minimum with Surface profile not more than 75 Microns. " |
| Applicable Industry | Maintanance / OEM |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | As a primer or shop coat primer for steel surface. |
| Description | It is a two pack primer based on Epoxy resin and Zinc Phosphate / Zinc Chrome Pigment. It gives a good protection in chemical and corrosive atmosphere. |
| Volume Solids | 40% ± 2 |
| DFT | 30-40 microns |
| Mixing Ratio | BASE HARD. 3 : 1 |
| Pot Life | 6-7 hrs. at 30OC and 65% relative humidity |
| Spreading Rate | 10 - 13 sq.m./ltr |
| Surface Dry | 2 - 3 hrs. at 30OC and 65% relative humidity |
| Hard Dry | 8 hrs at 30OC and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 8 hrs at 30OC and 65% relative humidity |
| RECOATING TIME - MAX | 4 months |
| Fully Cured | 7 Days |
| Shelf Life | Base: 12 months Hardner: 6 months |
| Surface Preparation | "Recommended surface should be free from oil, grease, salt and any other foreign matter Blast clean to Sa2½ minimum with Surface profile not more than 75 Microns. " |
| Applicable Industry | Maintanance / OEM |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlepoxy Thinner |
| Sugested Use | It is used for all steel surfaces as an efficient anticorrosive primer. |
20 & 21, Universal Industrial Estate, Sajgoan
Taluka: Khalapur District: RaigadState:Maharashtra - 410 203
Factory: (02192) 263244