Harlequinpaints

Grade	Industrial Grade 1
Drying System	Air Drying Clear Coat
Description	It is a two pack clear seaming compound based on Epoxy resin and polyamine based curing agent. It gives a Good seaming in various solvents and corrosive chemical.
Volume Solids	38 /-2 %
DFT	N/A
Mixing Ratio	BASE : HARDNER 1:1
Pot Life	4 Hrs Minimum
Spreading Rate	N/A
Surface Dry	20-30 mints @ 30Â°C and 65% relative humidity
Hard Dry	8-10 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	8 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Glossy
Shelf Life	Base: 12 months Hardner: 12 months
Surface Preparation	Recommended surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging
Application Method	Brushing/Airless spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For seaming compound in Fabrication Industries, packaging industry where good solvent and chemicals resistance is necessary.

Grade	Industrial Grade 2
Drying System	Air Drying Clear Coat
Description	It is a two pack clear seaming compound based on Epoxy resin and polyamide curing agent. It gives a good seaming in some solvents and corrosive chemical.
Volume Solids	50 /-2 %
DFT	N/A
Mixing Ratio	BASE : HARDNER 1:1
Pot Life	4 Hrs Minimum
Spreading Rate	N/A
Surface Dry	0.5-1 hr. @ 30Â°C and 65% relative humidity
Hard Dry	8-10 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	8 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Glossy
Shelf Life	Base: 12 months Hardner: 12 months
Surface Preparation	Recommended surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging
Application Method	Brushing/Airless spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Sugested Use	For seaming compound in Fabrication Industries, packaging industry, etc

Grade	Performance Grade
Drying System	Air Drying Clear Coat
Description	It is a two pack clear seaming compound based on Special Epoxy resin and polyamide adduct based curing agent. It gives a excellent seaming in various solvents and corrosive chemical .
Volume Solids	1
DFT	N/A
Mixing Ratio	BASE : HARDNER 2:1
Pot Life	4 Hrs Minimum
Spreading Rate	N/A
Surface Dry	1-2 Hrs @ 30Â°C and 65% relative humidity
Hard Dry	10-12 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	8 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Glossy
Shelf Life	Base: 12 months Hardner: 12 months
Surface Preparation	Recommended surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging
Application Method	Brushing/Airless spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For seaming compound in Fabrication Industries, packaging industry where excellent and durable solvent and chemicals resistance is necessary.

Grade	Performance Grade
Drying System	Air Drying Top Coat
Description	It is a two pack finish paint based on Epoxy resin and polyamide curing agent. It gives a good protection in chemical and corrosive atmosphere.
Volume Solids	48 /-2 %
DFT	20-25 Âµm per coat
Mixing Ratio	BASE : HARDNER 4:1 OR 3:1
Pot Life	4 Hrs Minimum
Spreading Rate	22-30 mÂ²/L
Surface Dry	0.5-1 hr. @ 30Â°C and 65% relative humidity
Hard Dry	10-12 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	16 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Semi Glossy to matt
Shelf Life	Base: 1 year Hardner: 6 months
Surface Preparation	Recommended primed surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For high quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants and Automobile Industry

Grade	Industrial Grade 2
Drying System	Air Drying Top Coat
Description	It is a two pack finish paint based on Epoxy resin and poly amide or amine curing agent. It gives a excellent protection in chemical and corrosive atmosphere.
Volume Solids	42 /-2 %
DFT	20-25 Âµm per coat
Mixing Ratio	BASE : HARDNER 4:1 OR 3:1
Pot Life	4 Hrs Minimum
Spreading Rate	17-21 mÂ²/L
Surface Dry	1-1.5 hr. @ 30Â°C and 65% relative humidity
Hard Dry	12-14 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	16 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Semi Glossy to matt
Shelf Life	Base: 1 year Hardner: 6 months
Surface Preparation	Recommended primed surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For Good quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants and Automobile Industry

Grade	Industrial Grade 2
Drying System	Air Drying Top Coat
Description	It is a two pack finish paint based on fortified Epoxy resin and polyamide curing agent. It gives a fair protection in chemical and corrosive atmosphere. With excellent drying and coverage property
Volume Solids	50 /-2 %
DFT	20-25 Âµm per coat
Mixing Ratio	BASE : HARDNER 4 : 1 OR 3:1
Pot Life	6 Hrs Minimum
Spreading Rate	20-25 mÂ²/L
Surface Dry	15-20mints. @ 30Â°C and 65% relative humidity
Hard Dry	12-14 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	16 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Full Glossy / Semi Glossy to matt
Shelf Life	Base: 1 year Hardner: 6 months
Surface Preparation	Recommended primed surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	6 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Sugested Use	For quality coating for Fabrication Industries, Machine Tool Industry, chemical industry, at economic cost etc

Grade	Performance Grade
Drying System	Air Drying Under Coat
Description	It is a two pack primer based on Epoxy resin and Zinc Phosphate or Zinc Chrome Pigment. It gives a excellent protection in chemical and corrosive atmosphere.
Volume Solids	42 /-2 %
DFT	30-35 Âµm per coat
Mixing Ratio	BASE : HARDNER 4:1 OR 3:1
Pot Life	4 Hrs Minimum
Spreading Rate	12-14 mÂ²/L
Surface Dry	0.5-1 hr. @ 30Â°C and 65% relative humidity
Hard Dry	8-10 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	10 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform matt
Shelf Life	Base: 1 year Hardner: 6 months
Surface Preparation	New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter.
Applicable Industry	Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For high quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants and Automobile Industry

Grade	Industrial Grade 2
Drying System	Air Drying Under Coat
Volume Solids	42 /-2 %
Description	It is a two pack primer based on Epoxy resin and polyamide curing agent. It gives a good protection in chemical and corrosive atmosphere.
DFT	30-35 Âµm per coat
Mixing Ratio	BASE : HARDNER 4:1 OR 3:1
Pot Life	4 Hrs Minimum
Spreading Rate	12-14 mÂ²/L
Surface Dry	0.5-1 hr. @ 30Â°C and 65% relative humidity
Hard Dry	12-14 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	10 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform matt
Shelf Life	Base: 1 year Hardner: 6 months
Surface Preparation	New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter.
Applicable Industry	Packaging/Automobile-OEM Engineering/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For Good quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants and Automobile Industry

Grade	Industrial Grade 1
Drying System	Air Drying Under Coat
Description	It is a single pack primer based on specialised Epoxy resin and curing agent. It gives a good protection in chemical and corrosive atmosphere.
Volume Solids	42 /-2 %
DFT	30-35 Âµm per coat
Mixing Ratio	N/A
Pot Life	N/A
Spreading Rate	12-14 mÂ²/L
Surface Dry	15-20 mints. @ 30Â°C and 65% relative humidity
Hard Dry	6-8 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	10 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform to matt
Shelf Life	1 Year
Surface Preparation	New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter.
Applicable Industry	Packaging/Automobile-OEM Engineering/ General Maintenance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	N/A
Recommended Thinner	Harlepoxy Thinner
Sugested Use	For moderate quality protective coating , Fabrication Industries, Machine Tool Industry, chemical industry, steel plants.

Grade	Industrial Grade 2
Drying System	Air Drying Under Coat
Description	It is a two pack primer based on Epoxy resin and polyamide curing agent. It gives a fair protection in chemical and corrosive atmosphere.
Volume Solids	38 /-2
DFT	30-35 Âµm per coat
Mixing Ratio	BASE : HARDNER 4:1 OR 3:1
Pot Life	4 Hrs Minimum
Spreading Rate	11-13 mÂ²/L
Surface Dry	0.5-1 hr. @ 30Â°C and 65% relative humidity
Hard Dry	12-14 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	10 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform matt
Shelf Life	Base: 1 year Hardner: 6 months
Surface Preparation	New Surface: Surface should be free from oil, grease, salt and any other foreign matter. Clean the surface mechanically or manually. Maintanance: Manual cleaning to remove any loose particle oil, grease and any other foreign matter.
Applicable Industry	Packaging/OEM Engineering/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	4 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Sugested Use	For fair quality protective coating , Fabrication Industries, Machine Tool Industry, steel plants,etc

Grade	Industrial Grade 1
Drying System	Air Drying Under Coat
Description	It is a two pack clear primer based on Epoxy resin and polyamide curing agent. It gives a good protection in chemical and corrosive atmosphere.
Volume Solids	38 /-2 %
DFT	25-30 Âµm per coat
Mixing Ratio	BASE : HARDNER 2:1 OR 3:1
Pot Life	5 Hrs Minimum
Spreading Rate	12-15 mÂ²/L
Surface Dry	0.5-1 hr. @ 30Â°C and 65% relative humidity
Hard Dry	12-14 hrs @ 30Â°C and 65% relative humidity
Tack Free	Overnight
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	10 Hrs
Recoating Time - MAX	7 Days
Finish	Smooth Uniform Glossy
Shelf Life	Base: 12 months Hardner: 12 months
Surface Preparation	New Steel: Recommended for abrasive blasting to Sa2Â½. If steel is coated by shop primer, clean all damages to shop primer and also clean the surface free from oil grease and any other foreign particles. Maintenance: Remove oil, grease etc with a detergent wash. Remove salt and other contaminants by high pressure fresh water hosing. Remove all rust and loose materials by abrasive blasting or mechanical cleaning. Dust off residues. For best results remove all loose rust by wire brushing and chipping.
Applicable Industry	Packaging/construction industry/ General Maintainance/Electronic and Electrical
Application Method	Conventional Air Spray/ Brushing / Airless Spray
Gel Time	5 Hrs Minimum
Recommended Thinner	Harlepoxy Thinner
Suggested Use	For good quality concrete primer. It protects concrete from ingress of moisture and fortifies the concrete strength.

Grade	Performance Grade
Drying System	Stoving Lacquer
Description	It is Epoxy-Phenolic based pigmented Lacquer having excellent resistance to chemicals and some solvents with food grade properties.
Volume Solids	45 /-2 %
DFT	15-20 Âµm per coat
Mixing Ratio	N/A
Pot Life	N/A
Spreading Rate	22-30 mÂ²/L depending on Shade
Surface Dry	Immidiate
Hard Dry	Immidiate
Tack Free	Immidiate
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	2 Hrs
Recoating Time - MAX	None
Shelf Life	6 months
Finish	Smooth and Uniform with glossy
Surface Preparation	Recommended surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging
Application Method	Conventional Air Spray/ Airless Spray
Gel Time	N/A
Recommended Thinner	Harlepoxy Thinner
Suggested Use	As a interior lacquer for barrels, drums and tins used for packing of chemicals. It also can be used for containers used for storage of Food products.

Grade	Performance Grade
Drying System	Stoving Lacquer
Description	It is Epoxy-Phenolic based clear Lacquer having excellent resistance to chemicals and some solvents with food grade properties.
Volume Solids	30 /-2 %
DFT	15-20 Âµm per coat
Mixing Ratio	N/A
Pot Life	N/A
Spreading Rate	15-20 mÂ²/L
Surface Dry	Immidiate
Hard Dry	Immidiate
Tack Free	Immidiate
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	2 Hrs
Recoating Time - MAX	None
Finish	Smooth and Uniform with glossy
Shelf Life	6 months
Surface Preparation	Recommended surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging
Application Method	Conventional Air Spray/ Airless Spray
Gel Time	N/A
Recommended Thinner	Harlepoxy Thinner
Suggested Use	As a interior lacquer for barrels, drums and tins used for packing of chemicals. It also can be used for containers used for storage of Food products.

Grade	Industrial Grade 1
Drying System	Stoving Lacquer
Description	It is Epoxy-Phenolic based clear Lacquer having Good resistance to chemicals and some solvents with food grade properties.
Volume Solids	32 /-2 %
DFT	15-20 Âµm per coat
Mixing Ratio	N/A
Pot Life	N/A
Spreading Rate	16-21 mÂ²/L depending on Shade
Surface Dry	Immidiate
Hard Dry	Immidiate
Tack Free	Immidiate
Subsequent Coat	As per substrate condition recommended coating system
Recoating Time - MIN	2 Hrs
Recoating Time - MAX	None
Finish	Smooth and Uniform with glossy
Shelf Life	6 months
Surface Preparation	Recommended surface should be free from oil, grease, salt and any other foreign matter.
Applicable Industry	Packaging
Application Method	Conventional Air Spray/ Airless Spray
Gel Time	N/A
Recommended Thinner	Harlepoxy Thinner
Suggested Use	As a interior lacquer for barrels, drums and tins used for packing of chemicals. It also can be used for containers used for storage of Food products at economical cost.