| Description | This is chlorinated rubber based coating fortified with micaceous iron oxide pigment. It has good resistance to salt water |
| Volume Solids | 45% ± 2 |
| DFT | 50 Microns |
| Mixing Ratio | N/A |
| Pot Life | N/A |
| Spreading Rate | 9 Sq.m/ltr |
| Surface Dry | 1-2 Hrs at 30°C and 65% relative humidity |
| Hard Dry | 5-6 Hrs at 30°C and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 7 Hrs |
| RECOATING TIME - MAX | None |
| Fully Cured | 48 Hrs |
| Shelf Life | 1 Year |
| Surface Preparation | Properly primed surface, clean from oil, grease |
| Applicable Industry | Maintanance |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlechlor Thinner |
| Sugested Use | Recommended to use as intermediate in the chlorinated rubber coating system. |
| Description | It is a Chlorinated Rubber based Zinc Chromate or Zinc phosphate based primer having very good anti-corrosive properties with moderate chemicals resistance. |
| Volume Solids | 40% ± 2 |
| DFT | 30-40 microns |
| Mixing Ratio | N/A |
| Pot Life | N/A |
| Spreading Rate | 10-13Sq.m/ltr |
| Surface Dry | 1 Hrs @ 30°C and 65% relative humidity |
| Hard Dry | 6-8 Hrs @ 30°C and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 8 hrs at 30°C and 65% relative humidity |
| RECOATING TIME - MAX | None |
| Fully Cured | 48 Hrs |
| Shelf Life | 1 Year |
| Surface Preparation | Recommended to blast cleaning to Sa2-½ for new surface |
| Applicable Industry | Maintanance |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlechlor Thinner |
| Sugested Use | Recommended to use for structural steel in chemical and marine environment. |
| Description | It is Chlorinated Rubber suitably plasticized coating giving excellent adhesion and moderate resistant to industrial environment. |
| Volume Solids | 40% ± 2 |
| DFT | 30-40 microns |
| Mixing Ratio | N/A |
| Pot Life | N/A |
| Spreading Rate | 10.0 – 13 Sq.m/ltr |
| Surface Dry | 1 Hrs at 30°C and 65% relative humidity |
| Hard Dry | 6-8 Hrs at 30°C and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 6 Hrs |
| RECOATING TIME - MAX | None |
| Fully Cured | 48 Hrs |
| Shelf Life | 1 Year |
| Surface Preparation | Properly primed surface, free from oil, grease |
| Applicable Industry | Maintanance |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlechlor Thinner |
| Recommended Thinner | Harlechlor Thinner |
| Suggested Use | Recommended to use in saline and industrial atmosphere. |
| Description | It is chlorinated rubber based high build finish paint which gives a good wear |
| Volume Solids | 50% ± 2 |
| DFT | 50 Microns |
| Mixing Ratio | N/A |
| Pot Life | N/A |
| Spreading Rate | 10 Sq.m/ltr |
| Surface Dry | 2-4 Hrs at 30°C and 65% relative humidity |
| Hard Dry | 8-10 Hrs at 30°C and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 12 Hrs |
| RECOATING TIME - MAX | None |
| Fully Cured | 48 Hrs |
| Shelf Life | 1 Year |
| Surface Preparation | Properly primed surface, clean from oil, grease |
| Applicable Industry | Maintanance |
| Application Method | Brush/ Airless Spray |
| Recommended Thinner | Harlechlor Thinner |
| Sugested Use | Suggested to use in moderate corrosive atmosphere in Industrial and marine environment. |
| Description | It is Chlorinated Rubber modified coating with moderate weather resistant property. |
| Volume Solids | 33% ± 2 |
| DFT | 35 Microns |
| Mixing Ratio | N/A |
| Pot Life | N/A |
| Spreading Rate | 8.5 – 10 Sq.m/ltr |
| Surface Dry | 1-2 Hrs at 30°C and 65% relative humidity |
| Hard Dry | 7-8 Hrs at 30°C and 65% relative humidity |
| Subsequent Coat | As per substrate condition recommended coating system |
| RECOATING TIME - MIN | 10 Hrs |
| RECOATING TIME - MAX | None |
| Fully Cured | 48 Hrs |
| Shelf Life | 1 Year |
| Surface Preparation | Properly primed surface, clean from oil, grease |
| Applicable Industry | Maintanance |
| Application Method | Conventional Air Spray/ Brush/ Airless Spray |
| Recommended Thinner | Harlechlor Thinner |
| Sugested Use | Suggested to use in moderate corrosive atmosphere in Industrial and marine environment. |
20 & 21, Universal Industrial Estate, Sajgoan
Taluka: Khalapur District: RaigadState:Maharashtra - 410 203
Factory: (02192) 263244